Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Brass". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average of brass materials. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods
Scroll Right →
| Physical Properties |
Metric |
English |
Comments |
| Density |
7.60 - 8.75 g/cc |
0.275 - 0.316 lb/in³ |
Average value: 8.48 g/cc Grade Count:291 |
Scroll Right →
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Rockwell B |
25.0 - 133 |
25.0 - 133 |
Average value: 69.8 Grade Count:165 |
| Hardness, Rockwell F |
54.0 - 100 |
54.0 - 100 |
Average value: 68.7 Grade Count:64 |
| Hardness, HR30T |
8.00 - 240 |
8.00 - 240 |
Average value: 51.8 Grade Count:105 |
| Tensile Strength, Ultimate |
159 - 896 MPa |
23000 - 130000 psi |
Average value: 440 MPa Grade Count:300 |
| Tensile Strength, Yield |
69.0 - 683 MPa |
10000 - 99100 psi |
Average value: 247 MPa Grade Count:268 |
| Elongation at Break |
3.00 - 68.0 % |
3.00 - 68.0 % |
Average value: 35.4 % Grade Count:296 |
| Reduction of Area |
40.0 - 60.0 % |
40.0 - 60.0 % |
Average value: 52.4 % Grade Count:53 |
| Modulus of Elasticity |
97.0 - 115 GPa |
14100 - 16700 ksi |
Average value: 104 GPa Grade Count:264 |
| Poissons Ratio |
0.280 - 0.375 |
0.280 - 0.375 |
Average value: 0.318 Grade Count:235 |
| Charpy Impact |
43.0 - 69.0 J |
31.7 - 50.9 ft-lb |
Average value: 48.8 J Grade Count:98 |
| Izod Impact |
43.0 - 45.0 J |
31.7 - 33.2 ft-lb |
Average value: 44.0 J Grade Count:22 |
| Fatigue Strength |
22.0 - 360 MPa |
3190 - 52200 psi |
Average value: 106 MPa Grade Count:93 |
| Machinability |
30.0 - 106 % |
30.0 - 106 % |
Average value: 45.7 % Grade Count:273 |
| Shear Modulus |
35.0 - 44.0 GPa |
5080 - 6380 ksi |
Average value: 39.1 GPa Grade Count:259 |
| Shear Strength |
205 - 415 MPa |
29700 - 60200 psi |
Average value: 273 MPa Grade Count:208 |
Scroll Right →
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
0.00000470 - 0.0000280 ohm-cm |
0.00000470 - 0.0000280 ohm-cm |
Average value: 0.00000678 ohm-cm Grade Count:246 |
| Magnetic Susceptibility |
-1.00e-6 |
-1.00e-6 |
Average value: -1.00e-6 Grade Count:40 |
Scroll Right →
| Thermal Properties |
Metric |
English |
Comments |
| CTE, linear |
18.7 - 26.0 µm/m-°C |
10.4 - 14.4 µin/in-°F |
Average value: 20.4 µm/m-°C Grade Count:281 |
| Specific Heat Capacity |
0.375 - 0.380 J/g-°C |
0.0896 - 0.0908 BTU/lb-°F |
Average value: 0.380 J/g-°C Grade Count:254 |
| Thermal Conductivity |
26.0 - 159 W/m-K |
180 - 1100 BTU-in/hr-ft²-°F |
Average value: 119 W/m-K Grade Count:285 |
| Melting Point |
820 - 1030 °C |
1510 - 1880 °F |
Average value: 917 °C Grade Count:264 |
| Solidus |
820 - 990 °C |
1510 - 1810 °F |
Average value: 904 °C Grade Count:286 |
| Liquidus |
890 - 1030 °C |
1630 - 1880 °F |
Average value: 930 °C Grade Count:286 |
Scroll Right →
| Processing Properties |
Metric |
English |
Comments |
| Processing Temperature |
260 °C |
500 °F |
Average value: 260 °C Grade Count:5 |
| Annealing Temperature |
425 - 750 °C |
797 - 1380 °F |
Average value: 538 °C Grade Count:253 |
| Hot-Working Temperature |
625 - 900 °C |
1160 - 1650 °F |
Average value: 770 °C Grade Count:226 |
| Recrystallization Temperature |
10.0 - 400 °C |
50.0 - 752 °F |
Average value: 237 °C Grade Count:214 |
Scroll Right →
| Component Elements Properties |
Metric |
English |
Comments |
| Antimony, Sb |
0.0200 - 0.100 % |
0.0200 - 0.100 % |
Average value: 0.0600 % Grade Count:20 |
| Copper, Cu |
55.0 - 86.0 % |
55.0 - 86.0 % |
Average value: 66.4 % Grade Count:299 |
| Silicon, Si |
3.50 - 4.50 % |
3.50 - 4.50 % |
Average value: 4.00 % Grade Count:5 |
| Tin, Sn |
0.250 - 5.00 % |
0.250 - 5.00 % |
Average value: 0.783 % Grade Count:100 |
| Zinc, Zn |
5.00 - 43.5 % |
5.00 - 43.5 % |
Average value: 32.7 % Grade Count:299 |